摘要
Ca8Mg(SiO4)4Cl2:Eu2+ phosphor doped with Sr2+ cation for Ca2+ partially, was synthesized by solid-state reaction at high temperature under reducing atmosphere, and its luminescent properties were investigated. The experimental results indicate that the emission intensity of the phosphor increases after being doped with a few amount of Sr2+ ion. The emission peak of the phosphor blue shift to about 464 nm when the phosphor is doped with large quantity of Sr2+ ions. The excitation spectrum indicates that the phosphor can be well excited by UV and blue light from 300 to 460 nm, and the phosphor was fitted well for the excitation by UV or blue-LED.
Ca8Mg(SiO4)4Cl2:Eu2+ phosphor doped with Sr2+ cation for Ca2+ partially, was synthesized by solid-slate reaction at high temperature under reducing atmosphere, and its luminescent properties were investigated. The experimental results indicate that the emission intensity of the phosphor increases after being doped with a few amount of Sr2+ ion. The emission peak of the phosphor blue shift to about 464 nm when the phosphor is doped with large quantity of Sr2+ ions. The excitation spectrum indicates that the phosphor can be well excited by UV and blue light from 300 to 460 nm, and the phosphor was fitted well for the excitation by UV or blue-LED.
基金
Project supported by the National Natural Science Foundation of China (50372086)
MOST of China (2006CB601104)