摘要
A series of Ce2-xPrxFe16.5Co0.5 alloys were prepared by arc melting under purified argon atmosphere. The structure and magnetic entropy changes in Ce2-xPrxFe16.5Co0.5 alloys were investigated by means of X-ray diffraction pattern and MPMS XL-7 magnetometer. The experimental results show that the crystal structure of Ce2-xPrxFe16.5Co0.5 alloys keeps in Th2Zn17-type rhombohedral, and the Curie temperature of Ce2-xPrxFe16.5Co0.5 alloys can be shifted to room temperature around by a composition adjustment. The magnetic entropy changes (-ΔSM) in Ce2-xPrxFe16.5Co0.5 alloys are relatively large, and a platform of magnetic entropy changes appears near the temperature TC. Ce2-xPrxFe16.5Co0.5 alloys are the potential working media for magnetic refrigeration with their stable chemical properties and especially low price.
A series of Ce2-xPrxFe16.5Co0.5 alloys were prepared by arc melting under purified argon atmosphere. The structure and magnetic entropy changes in Ce2-xPrxFe16.5Co0.5 alloys were investigated by means of X-ray diffraction pattern and MPMS XL-7 magnetometer. The experimental results show that the crystal structure of Ce2-xPrxFe16.5Co0.5 alloys keeps in Th2Zn17-type rhombohedral, and the Curie temperature of Ce2-xPrxFe16.5Co0.5 alloys can be shifted to room temperature around by a composition adjustment. The magnetic entropy changes (-ΔSM) in Ce2-xPrxFe16.5Co0.5 alloys are relatively large, and a platform of magnetic entropy changes appears near the temperature TC. Ce2-xPrxFe16.5Co0.5 alloys are the potential working media for magnetic refrigeration with their stable chemical properties and especially low price.
基金
This work was financially supported by the Natural Science Foundation of Guangdong Province (No.05300306) and the Natural Science Foundation of the Guangdong Province, China (No.C013003).