溶胶-凝胶法制备YBa2Cu3O7材料的结构与性能特点
Structure and performance of YBa2Cu3O7 prepared by sol-gel methods
摘要
用溶胶-凝胶法制取的Y-Ba-Cu-O粉体作为原料,压制成型并经960℃高温烧结及缓慢冷却,可以制备得到高温超导的YBa2Cu3O7样品,其超导临界转变温度为92K,无外磁场的液氮温度条件下的临界电流密度为400A/cm2.交流磁化率的测试说明样品具备较好的抗磁性.
出处
《功能材料》
EI
CAS
CSCD
北大核心
2004年第z1期898-902,906,共6页
Journal of Functional Materials
参考文献8
-
1[2]Bednora J G, Muller K A. [J]. Z Phys, 1986,64: 189.
-
2[3]Wu M K, Ashburn J R, Timg C J, et al. [J]. Phys Rev Lett,1987, 58: 908.
-
3[4]Kresin V Z, WolfS A. [J]. Phys Rev, 1992, 46: 6458.Vreit V, Schweiss P, Hauff R, et al. [J]. Physi Rev, 1995, 52:15727.
-
4[6]Cava R J, Batlogg B, Sunshine S A, et al. [J]. Physica, 1988,153-155: 560.
-
5[7]Xiao G, Cieplak M Z, Gavin A, et al. [J]. Phys Rev Lett,1988, 60: 1446.
-
6[9]Gyorgy E M, et al. [J]. Appl Phys Lett, 1989, 55: 283.
-
7[10]Kwok W K, et al. [J]. Phys Rev Lett, 1990, 64: 966.
-
8[11]Zhu Y, Suenaga M, Inshinde S L, Rudman D A, ed.Interfaces in High-Tc Superconducting Systems. [M]. New York: Springer-Verlag, 1994, 140.
-
1刘宝珠,张贵德,刘录,李秀农,姜新德.Y Ba_2Cu_3O_(7-x)高温超导片的制备[J].黑龙江大学自然科学学报,1992,9(1):79-81. 被引量：1
-
2布凤山,张红.YBCO高T_c超导屏蔽筒的制备[J].稀有金属,1998,22(3):235-237.
-
3郭志超,李平林.晶粒细化对MgB_2超导临界电流密度的作用[J].物理学报,2014,63(6):249-254.
-
4柴永泉,靳常青,刘邦贵.类MgB_2硼化物晶体电子结构比较研究[J].物理学报,2003,52(11):2883-2889. 被引量：10
-
5刘志明.高温超导电力技术展望[J].大众用电,2003(8):22-23. 被引量：2
-
6张家权,李法科,潘孝仁.高温超导体YBa_2Cu_3O_(7-x)的结构、形貌和性质[J].华东化工学院学报,1989,15(3):384-388.
-
7任学平,王连忠.变形与超导[J].塑性工程学报,1997,4(3):66-73.
-
8张志强.煤矿供电系统无功功率补偿和谐波治理[J].电力学报,2009,24(4):306-310. 被引量：5
-
9侯碧辉,彭鹏,易俗,许勤论,陈慧余,沈保根.LaBaMnO薄膜磁性测量中抗磁性衬底的扣除[J].物理测试,1998,16(3):30-32.
-
10靳常青.高温高压合成顶角氧掺杂型高温超导系列[J].高压物理学报,2004,18(1):4-9. 被引量：3