摘要
The interfacial binding covalent bond density (CBD) and the local environmental total bond order (LTBO) of the Ni/Ni3Alinterface with different lattice misfits (δ) were calculated by using first-principles discrete variation Xα method. It was foundthat the effects of lattice misfits on the electronic structures of incoherent Ni/Ni3Al interface were very obvious. On one hand,less than -0.6% negative lattice misfit can promote the binding strength of γ/γ′ interface. On the other hand, the totalbonding strength of γ/γ′ interface decreases with increasing δ. Therefore, the magnitude and sign of lattice misfit must becarefully controlled for balancing the high temperature creep strength of Ni-base single crystal superalloy and the structuralstability of γ/γ′interface when one designs a new Ni-base single crystal superalloy.