超细Nb_20_5粉末的研制

Preparation of Ultrafine Nb_2O_5 Powder

对采用均匀沉淀法制备陶瓷电容器级(平均粒径为0.1-0.2μm的超细粉末)Nb2O5粉末的最佳工艺条件进行了探讨,研究了均匀沉淀过程中,反应温度、沉淀终点pH值、反应物浓度、脱水剂和添加剂以及焙烧温度对Nb(OH)5粉体粒度分布及粒径的影响。利用TG-DTA、SEM、XRD、比表面积测试仪(BET)和CILAS粒度测试仪进行了测定,结果表明:当H2NbOF5浓度在0.2~0.4M时,以NH3·H2O作沉淀剂,用乙醇、丙酮等作脱水剂,所获沉淀在80~100℃干燥后,制备的Nb(OH)5粉体粒度均匀且分布窄,其平均粒径为0.07 μm,经700℃焙烧后,可制得粒度分布窄、团聚少、比表面积为14.44 m2/g、平均粒径为0.1 μm,且纯度>99.95%的陶瓷电容器级Nb2O5微粉体。该方法具有设备简单、工艺流程短、污染小,产品纯度高等特点。

The optimum conditions were found for preparing the ceramic capacitor ultrafine Nb2O5 powder(average diameter0.1-0.2μm) by the homogeneous precipitation. The effect of the reaction temperature, the final pH value, the concentration of reactor, the type of dehydration and additive on the effect of Nb(OH)5 powder?size and distribution was as well as.It was proved by TG-DTA, TEM, SEM, XRD, BET and CILAS that the Nb(OH)5 particles were average (average diameter 0.07um) and its distribution was narrow after dryi...