摘要
The thermal barrier coatings with NiCrAlY alloy bonding layer, NiCrAlY Y 2O 3 stabilized ZrO 2 transition layer and Y 2O 3 stabilized ZrO 2 ceramic layer are prepared on nickel alloy substrates using the plasma spray technique. The relationship among the composition, structure and property of the coatings are investiga ted by means of optical microscope, scanning electronic microscope and the experiments of thermal shock resistance cycling and high temperature oxidation resistance. The results show that the structure design of introdu cing a transition layer between Ni alloy substrate and ZrO 2 ceramic coating guarantees the high quality and properties of the coatings; ZrO 2 coatings doped with a little SiO 2 possesses better thermal shock resistance and more excellent hot corrosion resistance as compared with ZrO 2 coating materials without SiO 2 ;the improvement in performance of ZrO 2 coating doped with SiO 2 is due to forming more dense coating structure by self closing effects of the flaws and pores in the ZrO 2 coatings.
The thermal barrier coatings with NiCrAlY alloy bonding layer, NiCrAlY-Y2O3 stabilized ZrO2 transition layer and Y2O3 stabilized ZrO2 ceramic layer are prepared on nickel alloy substrates using the plasma spray technique. The relationship among the composition, structure and property of the coatings are investigated by means of optical microscope, scanning electronic microscope and the experiments of thermal shock resistance cycling and high temperature oxidation resistance. The results show that the structure design of introducing a transition layer between Ni alloy substrate and ZrO2 ceramic coating guarantees the high quality and properties of the coatings; ZrO2 coatings doped with a little SiO2 possesses better thermal shock resistance and more excellent hot corrosion resistance as compared with ZrO2 coating materials without SiO2; the improvement in performance of ZrO2 coating doped with SiO2 is due to forming more dense coating structure by self- closing effects of the flaws and pores in the ZrO2 coatings.