锆合金包壳的碘致应力腐蚀研究
摘要
碘致应力腐蚀开裂被普遍认为是引起锆合金包壳与芯块之间相互作用失效的原因。本文拟就影响碘致应力腐蚀开裂的主要因素和开裂机理作一简要综述。
出处
《机械》
2002年第z1期203-204,共2页
Machinery
参考文献9
-
1[2]J.H.Davies. H.S.Rosenbaum,J.S.Armijo,E.Rosicky. E. L.Esch,S.B.Wisner, Procee dings of the ANS Topical Meeting on Water Reactor Fuel Perfonnance,ANS,St.Cherles, IL, 1997.p.230.
-
2[3]K. Une,J.Nucl.Mater.87( 1979)207.
-
3[4]B.Cox,J.C.Wood,Corrosion problems in energy conversion and generation,in:C.S.Tedmon Jr.(Ed.), The Electrochemical Society, 1974,p.275.
-
4[5]S.H.Shann,D.R. Olander, J.Nucl. Mater. 113(1983)23.
-
5[6]M.Nagai,S.Shimada, S.Nishimra,K. Amano,G.Yagawa, Elucidating the iodine stress corrosion craching process for Zircaloy tubing, Proceedigs of the IAEA Meeting on Pellet Cladding Interaction in Water Reactor Fuel,Seattle, 1983.
-
6[7]N,Fuhrman,Evaluation of Fuel Performance in Main Yankee Core 1-Task c,EPRI N P-218,EPRI,palo Alto,CA, 1976.
-
7[8]P.H.Kreyns. G Lspahr. J. E.McCauley.J.Nucl.Mater.61 (1976) 203.
-
8[9]B.Cox.J.Nucl. Mater. 170(1990)249.
-
9[10]R.Haddad,B.Cox,J.Nucl.Mater. 138(1986)81.
-
1崔旭梅,彭倩,李静媛,唐正华,李言荣.新锆合金碘致应力腐蚀性能研究[J].核动力工程,2004,25(2):128-132.
-
2崔旭梅,李言荣,陶伯万,刘兴钊,唐正华,彭倩.锆合金包壳的碘致应力腐蚀研究进展[J].材料导报,2004,18(11):40-43.
-
3彭倩,李卫军,唐正华,崔旭梅,衡雪梅.Zr-Sn-Nb合金的碘致应力腐蚀断口分析[J].电子显微学报,2004,23(4):494-494.
-
4彭倩,遆忠信,潘英,李聪,彭小明.锆合金的碘致应力腐蚀开裂研究(英文)[J].中国核科技报告,2003(3):90-104.
-
5石明华,李中奎,田锋,戴训,张建军,周军,王文生.NZ2锆合金碘致应力腐蚀[J].稀有金属材料与工程,2013,42(8):1722-1725.
-
6崔旭梅,唐正华,彭倩,李静媛.组织对N18新锆合金的碘致应力腐蚀行为的影响[J].四川大学学报（工程科学版）,2002,34(6):75-77. 被引量：5
-
7衡雪梅,彭倩.新锆合金包壳的碘致应力腐蚀研究[J].机械工程材料,2004,28(10):13-15.
-
8闫盟,尹祁伟,王鹏飞,梁波,王美玲.N36锆合金包壳管环向拉伸I-SCC行为评价(英文)[J].稀有金属材料与工程,2015,44(1):58-61.
-
9陈继林,胡亚民,莫伟灵,金道昌.Cr12MoV钢制摆辗模具芯块失效分析[J].兵器材料科学与工程,1991,14(10):49-53. 被引量：7
-
10钟多军.核燃料元件用锆合金包壳的焊接[J].山东工业技术,2017(5):10-10. 被引量：1