Study on Semi-solid Rheocasting Forming for Magnesium Alloy by Mechanical Stirring

In this paper the effect of pouring temperature of magnesium melt, preheating temperature of the barrel of screw mixer and shear rate on the solidified microstructures of semi-solid slurry was investigated by mechanical stirring method. The appropriate processing parameters of slurry preparation were obtained. The mold filling for thin walled casting was examined. Results indicated that the solid volume fraction of non-dendritic structure increased with decrease in pouring temperature of magnesium melt and the barrel preheating temperature of screw mixer. Also the grain size of primary α phase was reduced. Furthermore, the solid volume fraction of semi-solid non-dendritic structure decreased with the increase in shear rate. In the same time, grain size of primary α phase slightly changed. The fine-round granular solidified structure with 30～50 μm of prepared AZ91D magnesium semi-solid slurry was presented. Finally, it is successful to fabricate 1.0 mm extremely thin walled casting with clear contour and good soundness.

In this paper the effect of pouring temperature of magnesium melt, preheating temperature of the barrel of screw mixer and shear rate on the solidified microstructures of semi-solid slurry was investigated by mechanical stirring method. The appropriate processing parameters of slurry preparation were obtained. The mold filling for thin walled casting was examined. Results indicated that the solid volume fraction of non-dendritic structure increased with decrease in pouring temperature of magnesium melt and ...