The joint of 40Cr steel and TiAl based alloy has been studied by means of a high frequency induction diffusion welder. The experimental results show that, the higher the temperature and pressure, the higher the strength of the joints. The optimum parameters are: T=1123~1323 K. t=10~30 min, P=5-20 MPa.
The joint of 40Cr steel and TiAl based alloy has been studied by means of a high frequency induction diffusion welder. The experimental results show that, the higher the temperature and pressure, the higher the strength of the joints. The optimum parameters are: T=1123~1323 K. t=10~30 min, P=5-20 MPa.