Zn∶In∶Fe∶LiNbO_3晶体的生长及其二波耦合效应的研究

Growth of Zn∶In∶Fe∶LiNbO_3 and Research of Its Two Wave Couple Effect

ZnO(4mol%),In 2O 3(1mol%)and Fe 2O 3(0.05mol%)were doped in LiNbO 3 and Czochralski method was used to grow Zn∶In∶Fe∶LiNbO 3 crystal.The diameter of the crystal we grew is 30mm.The technology parameter we took is that the axial temperature gradient is 40℃/cm,the growth rate is 1mm/h, the rotation rate is 15-25r/min,the temperature of polarization is 1220℃ and the current density of polarization is 5mA/cm 2.The wafer dimension is 10mm×10mm×3mm and was covered in Li 2CO 3 powder to reduce.The reduction temperature is 500℃ and reduction time is 30 hours. OH - stretch vibration transmission spectra were measured by Fourier infrared spectrophotometer. There are two absorption peaks in OH - spectra of Zn∶In∶Fe∶LiNbO 3,in which one is at 3534cm -1 (2.83μm) and the other is at 3505cm -1 (2.85μm).The peak at 2.85μm is far lower than that at 2.83μm. Because of the threshold effect of Zn 2+ and In 3+ ,the peak at 2.83μm is generated and the peak at 2.85μm is related with Fe 3+ .In LiNbO 3 only doped with Fe,Li + site is taken place by Fe 3+ .When doping Zn 2+ and In 3+ in high concentration,these two ions take place Nb that is at Li site and Fe 3+ substitutes for Nb 5+ at the same time.The interaction between Fe 3+ and OH - make the OH - peak shift to 2.85μm.

ZnO(4mol%),In 2O 3(1mol%)and Fe 2O 3(0.05mol%)were doped in LiNbO 3 and Czochralski method was used to grow Zn∶In∶Fe∶LiNbO 3 crystal.The diameter of the crystal we grew is 30mm.The technology parameter we took is that the axial temperature gradient is 40℃/cm,the growth rate is 1mm/h, the rotation rate is 15-25r/min,the temperature of polarization is 1220℃ and the current density of polarization is 5mA/cm 2.The wafer dimension is 10mm×10mm×3mm and was covered in Li 2CO 3 powder to reduce.The redu...