摘要
Semiconducting SrTiO 3 based voltage sensing and dielectric ceramics were prepared by single step sintering with Li 2CO 3 SiO 2 as liquid phase additives.The effects of the content of liquid phase,the ratio of Li/Si and the sintering temperatures on properties were discussed in terms of electrical properties and microstructures of materials.The results showed thatSrTiO 3 based varistor ceramics,with 0.6 mol% Li 2CO 3 SiO 2(Li/Si=3/2) and sintered at 1 380 ℃ in graphite and N 2 reducing atomosphere,had excellent current volatage sensing and dielectric characteristics.
以 L i2 CO3-Si O2 为液相掺杂剂 ,采用一次烧成工艺 ,制备出半导体的 Sr Ti O3基压敏与介电性的双功能陶瓷 .通过电性能与微观结构分析 ,研究了液相掺杂浓度、L i/Si比值及烧结温度对材料性能的影响 .结果表明 ,以 6× 10 - 3mol/L的 Li2 CO3+ Si O2 为液相掺杂剂 ,L i/Si=3 /2 ,温度为 13 80℃时 ,在石墨和氮气形成的还原性气氛中烧成的 Sr Ti