摘要
Straw of seven rice varieties with early-, middle- and late maturity was collected from Huazhong Agricultural University in Hubei. A study was carried out for rice straw in the aspects of the characters of straw silicification and extraction biogenic silica (EBSi), the relationship between characters of EBSi and kinetic characteristics of degradation of fibrous components in fistulated cows, as well as the effect of urea treatment on rice straw desilicification. Although total silica content (ADISi) in rice straw was similar, the efficiency of extraction biogenic silica (EEBSi) and cellulose in early varieties were significantly higher than those in middle (18.9% and 9.1 %) and late ones (26.1% and 11.2%). The degradability of EBSi and cellulose of early varieties were higher than those of middle by 70.0% and 17.5%, and of late varieties by 47.8% and 23.7% , respectively. The in sacco degradability and in vitro VFA production of early varieties were also higher than those of middle by 14.5% and 19.0%, and late by 12.9% and 14.8%. Comparing the morphological fractions of the rice straws, EEBSi, cellulose content, and in vitro VFA production were different with the order of blade < sheath < stem. A significant correlation was found between the contents of EBSi and cellulose (r= 0.86), and the two contents were remarkably correlated with the potential straw degradability (a + b) by r = 0.90 and 0.84 respectively. Therefore, EBSi in rice straw was a main factor affecting the potential degradability of rice straw, rather than the ADISi of straw. Urea treatment improved rice straw degradability, degradation rate and potential degradability by 10.8% , 27.9% , and 10.1% respectively, compared to untreated straws.
Straw of seven rice varieties with early-, middle- and late maturity was collected from Huazhong Agricultural University in Hubei. A study was carried out for rice straw in the aspects of the characters of straw silicification and extraction biogenic silica (EBSi), the relationship between characters of EBSi and kinetic characteristics of degradation of fibrous components in fistulated cows, as well as the effect of urea treatment on rice straw desilicification. Although total silica content (ADISi) in rice straw was similar, the efficiency of extraction biogenic silica (EEBSi) and cellulose in early varieties were significantly higher than those in middle (18.9% and 9.1 %) and late ones (26.1% and 11.2%). The degradability of EBSi and cellulose of early varieties were higher than those of middle by 70.0% and 17.5%, and of late varieties by 47.8% and 23.7% , respectively. The in sacco degradability and in vitro VFA production of early varieties were also higher than those of middle by 14.5% and 19.0%, and late by 12.9% and 14.8%. Comparing the morphological fractions of the rice straws, EEBSi, cellulose content, and in vitro VFA production were different with the order of blade < sheath < stem. A significant correlation was found between the contents of EBSi and cellulose (r= 0.86), and the two contents were remarkably correlated with the potential straw degradability (a + b) by r = 0.90 and 0.84 respectively. Therefore, EBSi in rice straw was a main factor affecting the potential degradability of rice straw, rather than the ADISi of straw. Urea treatment improved rice straw degradability, degradation rate and potential degradability by 10.8% , 27.9% , and 10.1% respectively, compared to untreated straws.