摘要
Decomposition processes of the quenched Zn-Al alloys were studied by differential scanning calorimetry (DSC), X-ray diffraction (XRD) and transmission electron microscopy (TEM). The results show that the stabilities of supersaturated solid solution (SSS) of Zn-Al alloy and α' phase formed by quenching would reduce with the increase of Zn content and the precipitation of η-Zn phases even when aging at ambient temperature, so that the exothermic precipitation peak in DSC curve would disappear. The activation energy of the η-Zn precipitation and the reaction enthalpy were calculated and measured. The kinetics of α' decomposition or η-Zn formation was determined by XRD. The microstructure change during aging was observed by TEM.
Decomposition processes of the quenched Zn-Al alloys were studied by differential scanning calorimetry (DSC), X-ray diffraction (XRD) and transmission electron microscopy (TEM). The results show that the stabilities of supersaturated solid solution (SSS) of Zn-Al alloy and α' phase formed by quenching would reduce with the increase of Zn content and the precipitation of η-Zn phases even when aging at ambient temperature, so that the exothermic precipitation peak in DSC curve would disappear. The activation energy of the η-Zn precipitation and the reaction enthalpy were calculated and measured. The kinetics of α' decomposition or η-Zn formation was determined by XRD. The microstructure change during aging was observed by TEM.