摘要
The structures and macro-segregation of 2124 Al-alloy were studied when a pulsed magnetic field (PMF) was applied during solidification. It is found through experi-ments that a remarkable change occurs in the solidification structures of 2124 Al-alloy under pulsed magnetic field. The eutectic phase at grain boundaries change from thick continuous eutectic network to thin discontinuous one, and the distribution of solute elements was also homogenized. The typical negative segregation phenomenon of Cu in common solidification condition was restrained, and the segregation of Mg decreased.
The structures and macro-segregation of 2124 Al-alloy were studied when a pulsed magnetic field (PMF) was applied during solidification. It is found through experi-ments that a remarkable change occurs in the solidification structures of 2124 Al-alloy under pulsed magnetic field. The eutectic phase at grain boundaries change from thick continuous eutectic network to thin discontinuous one, and the distribution of solute elements was also homogenized. The typical negative segregation phenomenon of Cu in common solidification condition was restrained, and the segregation of Mg decreased.
基金
This research was supported by National Key Basic Research and Development Programme of China "973" (No. G19990649051).