摘要
By the increase in Mo content,the addition of microalloying elements V and Nb and by reducing the contents of Mn,P and S based on the composition of steel 42 CrMo,we have developed a 1 300 MPa-grade high strength steel(ADF1)for bolts.The sustained load bending test,sustained load tensile test and stress corrosion cracking test have been carried out to evaluate the delayed fracture resistance of steel ADFl and commercial steel 42 CrMo.The results showed that steel ADF1 has superior delayed fracture resistance to that of 42 CrMo steel.It's concluded that the superior delayed fracture resistance of ADF1 is mainly due to the increase of tempering temperature,fine homogeneously distributed MC carbide and fine prior austenite grain size.
By the increase in Mo content,the addition of microalloying elements V and Nb and by reducing the contents of Mn,P and S based on the composition of steel 42 CrMo,we have developed a 1 300 MPa-grade high strength steel(ADF1)for bolts.The sustained load bending test,sustained load tensile test and stress corrosion cracking test have been carried out to evaluate the delayed fracture resistance of steel ADFl and commercial steel 42 CrMo.The results showed that steel ADF1 has superior delayed fracture resistance to that of 42 CrMo steel.It's concluded that the superior delayed fracture resistance of ADF1 is mainly due to the increase of tempering temperature,fine homogeneously distributed MC carbide and fine prior austenite grain size.
基金
Sponsored by National Key Fundamental Research Project(G1998061503)