Based on quantitative microscopic examinations of welds and welding rate for different steels(40Cr and T10A) joint,which possess the ultra-fine microstructure after high frequency hardening(HFH) and salt-bath cyclic quenching(SCQ),the suitable defect grey scale threshold value was determined,and the welding rate of superplastic solid-state welding of different steels(40Cr and T10 A steel) was systematically inspected and analyzed by means of self-made ultrasonic imaging inspection system.The experimental results showed that the superplastic solid-state weld of different steels can be inspected more accurately,reliably and quickly by this system,and the results were in good accordance with that of metallographic observation.The welding rate of superplastic welding is in linear relation with tensile strength of joint.
Based on quantitative microscopic examinations of welds and welding rate for different steels(40Cr and T10A) joint,which possess the ultra-fine microstructure after high frequency hardening(HFH) and salt-bath cyclic quenching(SCQ),the suitable defect grey scale threshold value was determined,and the welding rate of superplastic solid-state welding of different steels(40Cr and T10 A steel) was systematically inspected and analyzed by means of self-made ultrasonic imaging inspection system.The experimental results showed that the superplastic solid-state weld of different steels can be inspected more accurately,reliably and quickly by this system,and the results were in good accordance with that of metallographic observation.The welding rate of superplastic welding is in linear relation with tensile strength of joint.
基金
Item Sponsored by Provincial Natural Science Foundation of Henan(984040900)
State Key Laboratory of Laser Technology([2001]0110)