The influence of strontium addition and solidification rate on eutectic grain structure in a near-eutectic Al-Si alloy was investigated. The characteristic temperature of eutectic nucleation (TN),minimum temperature prior to recalescence (TM),and the growth temperature (TG) during cooling were determined by quantitative thermal analysis. All characteristic temperatures were found to decrease continuously with increasing Sr content and solidification rate. Microstructural analysis also revealed that the eutectic grain size decreases with increasing Sr content and solidi fication rate. Such eutectic grain refinement is attributed to the increased actual under-cooling ahead of the liquid/solid interface during solidification.
The influence of strontium addition and solidification rate on eutectic grain structure in a near-eutectic Al-Si alloy was investigated. The characteristic temperature of eutectic nucleation (TN),minimum temperature prior to recalescence (TM),and the growth temperature (TG) during cooling were determined by quantitative thermal analysis. All characteristic temperatures were found to decrease continuously with increasing Sr content and solidifi cation rate. Microstructural analysis also revealed that the eutectic grain size decreases with increasing Sr content and solidification rate. Such eutectic grain refinement is attributed to the increased actual under-cooling ahead of the liquid/solid interface during solidification.
基金
supported by the National Natural Science Foundation of China under grant No. 50771031
the Early Research Foundation of Southeast University under grant No. XJ0612238