A new mixing method was developed for solid-state reaction synthesis of SrAl2O4:Eu2+,Dy3+ long afterglow phosphors.The morphology and crystal structure of the phosphors were analyzed with scanning electron microscope(SEM) and X-ray diffractometer(XRD).The excitation and emission spectra of the long afterglow phosphors were measured,and the main emission band was around 514 nm.The decay time of the product was measured and compared with the phosphors prepared using dry-mixing method and wet-mixing method.It ...
A new mixing method was developed for solid-state reaction synthesis of SrAl2O4:Eu2+,Dy3+ long afterglow phosphors.The morphology and crystal structure of the phosphors were analyzed with scanning electron microscope(SEM) and X-ray diffractometer(XRD).The excitation and emission spectra of the long afterglow phosphors were measured,and the main emission band was around 514 nm.The decay time of the product was measured and compared with the phosphors prepared using dry-mixing method and wet-mixing method.It ...
基金
supported by the Program for New Century Excellent Talents in the University of China (NCET-06-0179)