摘要
The electrode process of La(Ⅲ) at Mo electrode in the molten LiCl-KCl for temperatures ranging from 683 K to 773 K was studied by cyclic voltammetry and chronopotentiometry,respectively.The results showed that in the molten LiCl-KCl,reduction of La(Ⅲ) occurred in a step with a global exchange of three electrons.Cyclic voltammetry studies indicated that at a sweep rate lower than 0.2 V/s,the electroreduction of La(Ⅲ) to lanthanum metal was reversible and controlled by diffusion of La(Ⅲ).However,the process b...
The electrode process of La(Ⅲ) at Mo electrode in the molten LiCl-KCl for temperatures ranging from 683 K to 773 K was studied by cyclic voltammetry and chronopotentiometry,respectively.The results showed that in the molten LiCl-KCl,reduction of La(Ⅲ) occurred in a step with a global exchange of three electrons.Cyclic voltammetry studies indicated that at a sweep rate lower than 0.2 V/s,the electroreduction of La(Ⅲ) to lanthanum metal was reversible and controlled by diffusion of La(Ⅲ).However,the process b...
基金
supported by the National Basic Research Program of China (2007CB209900)