The compounds of iron substituted yttrium oxide systems have been prepared for the importance in the field of magneto electric materials.The polycrystalline samples of Y2–xFexO3–y(x=0.1,0.2) were prepared by solid-state reaction method.The single-phase formation of these compounds was confirmed by X-ray diffraction studies.It was found that the samples crystallized in tetragonal phase and the lattice parameters were calculated as a=1.0559(7) nm,c=1.0832(9) nm for Y1.9Fe0.1O3–y and a=1.0545(6) nm,c=1.0841(8)...
The compounds of iron substituted yttrium oxide systems have been prepared for the importance in the field of magneto electric materials.The polycrystalline samples of Y2–xFexO3–y(x=0.1,0.2) were prepared by solid-state reaction method.The single-phase formation of these compounds was confirmed by X-ray diffraction studies.It was found that the samples crystallized in tetragonal phase and the lattice parameters were calculated as a=1.0559(7) nm,c=1.0832(9) nm for Y1.9Fe0.1O3–y and a=1.0545(6) nm,c=1.0841(8)...