摘要
Properties of high absorbency and modulus (gel strength) were both needed in applications of superabsorbent polymer (SAP). Generally, the absorption characteristic and gel strength reach a crossover point for a given system. Beyond this point, a given property will show improvement at the expense of another property. To synthesize SAP with properties superior to this optimum value, further modification in the process becomes essential. In our post-treatment modification of superabsorbent polymer, neither the variety of the crosslinkers, nor their amount was found the effective factors to the polymer performance, but the liquor ratio of the treating liquid to polymer. The combination of the chemical treating and heat-treating method was also explored. But this didn’t put any positive effect on SAP’s properties.
Properties of high absorbency and modulus (gel strength) were both needed in applications of superabsorbent polymer (SAP). Generally, the absorption characteristic and gel strength reach a crossover point for a given system. Beyond this point, a given property will show improvement at the expense of another property. To synthesize SAP with properties superior to this optimum value, further modification in the process becomes essential. In our post-treatment modification of superabsorbent polymer, neither the variety of the crosslinkers, nor their amount was found the effective factors to the polymer performance, but the liquor ratio of the treating liquid to polymer. The combination of the chemical treating and heat-treating method was also explored. But this didn't put any positive effect on SAP's properties.
基金
Shanghaimunicipalscienceandtechnologydevelopmentfund(No .9912 110 31)andShanghaimunicipalkeydisciplineproject