摘要
Ti-incorporated mesoporous silica materials with pore diameters of 3-4 nm have been prepared via the co-hydrolysis and co-condensation reactions, that is the sol-gel reactions, of titanium (IV) tetrabutoxide and tetraethylorthosilicate in the presence of tartaric acid as template, followed by extraction with ethanol to remove the templatemolecules. The materials were characterized in detail by Fourier transform infrared spectroscopy, nitrogen adsorption-desorption test, powder X-ray diffraction, transmission electron microscopy and X-ray energy dispersive spectroscopy. Theresults indicate that the Ti-containing silica materials have large specific surface areas (ca. 1200 m^2 g^(-1)) and pore volumes(ca. 0.900 cm^3 g^(-1)). The mesoporosity arises from disordered interconnecting channels or pores. The Ti-incorporated silicasexhibit catalytic activity for the ring-opening polymerization of ε-caprolactone, otherwise, the pure mesoporous silicamaterial shows no catalytic activity under the identical conditions.
Ti-incorporated mesoporous silica materials with pore diameters of 3-4 nm have been prepared via the co-hydrolysis and co-condensation reactions, that is the sol-gel reactions, of titanium (IV) tetrabutoxide and tetraethylorthosilicate in the presence of tartaric acid as template, followed by extraction with ethanol to remove the templatemolecules. The materials were characterized in detail by Fourier transform infrared spectroscopy, nitrogen adsorption-desorption test, powder X-ray diffraction, transmission electron microscopy and X-ray energy dispersive spectroscopy. Theresults indicate that the Ti-containing silica materials have large specific surface areas (ca. 1200 m^2 g^(-1)) and pore volumes(ca. 0.900 cm^3 g^(-1)). The mesoporosity arises from disordered interconnecting channels or pores. The Ti-incorporated silicasexhibit catalytic activity for the ring-opening polymerization of ε-caprolactone, otherwise, the pure mesoporous silicamaterial shows no catalytic activity under the identical conditions.
基金
This work was supported by the National Natural Science Foundation of China (No. 29874002), and the Outstanding Young Scientist Award from the National Natural Science Foundation of China (No. 29825504).