摘要
X-ray photoelectron spectroscopy and Raman spectroscopy were' used to determine the chemical change of polyphenylsilsesquioxane (PPSQ) during pyrolysis in flowing nitrogen. Two temperature ranges were found for pyrolysed PPSQ below and above 600degreesC, respectively. The former is related to the rearrangement of PPSQ backbone and the latter reflects that most of backbone structure of PPSQ might be broken down and unorganized. Carbon formed in carbonization of PPSQ sample pyrolysed at 900degreesC should be sp(3) bonded carbon with crystallite size effects or defects.
X-ray photoelectron spectroscopy and Raman spectroscopy were' used to determine the chemical change of polyphenylsilsesquioxane (PPSQ) during pyrolysis in flowing nitrogen. Two temperature ranges were found for pyrolysed PPSQ below and above 600degreesC, respectively. The former is related to the rearrangement of PPSQ backbone and the latter reflects that most of backbone structure of PPSQ might be broken down and unorganized. Carbon formed in carbonization of PPSQ sample pyrolysed at 900degreesC should be sp(3) bonded carbon with crystallite size effects or defects.
基金
The National Natural Science Foundation of China (Grant No. 20074039) and National 863 High-technology Project as well as the Science Foundation of PPLAS(No, 00-B-01) are gratefully acknowledged for the financial support to this work.