摘要
An epoxy-terminated hyperbranched aromatic polyester (P3) was synthesized from a hyperbranched aromatic polyester containing carboxylic acid end groups (P1), which was derived from the condensation polymerization of the AB(2) monomer, 5-acetoxyisophthalic acid. Polymer P1 was converted into the polymeric acid chloride by reaction with thionyl chloride. The acid chloride was reacted with ethanol and glycidol to form a poly(ethyl ester) (P2) and an epoxy terminated material (P3), respectively. The reaction conditions in each step of these processes had to be controlled very carefully to avoid unwanted cross-linking reactions. The characterization of products and intermediates, including molecular weight distributions and thermal properties, are reported.
An epoxy-terminated hyperbranched aromatic polyester (P3) was synthesized from a hyperbranched aromatic polyester containing carboxylic acid end groups (P1), which was derived from the condensation polymerization of the AB(2) monomer, 5-acetoxyisophthalic acid. Polymer P1 was converted into the polymeric acid chloride by reaction with thionyl chloride. The acid chloride was reacted with ethanol and glycidol to form a poly(ethyl ester) (P2) and an epoxy terminated material (P3), respectively. The reaction conditions in each step of these processes had to be controlled very carefully to avoid unwanted cross-linking reactions. The characterization of products and intermediates, including molecular weight distributions and thermal properties, are reported.
基金
The project is supported by the EPSRC and the Youth Science Foundation of Shanghai Higher Education.