摘要
Amorphous poly (L-2-hydroxy-3-phenylpropanoic acid) (PLHPPA) was synthesized by the microwave-assisted polycondensation of L-2-hydroxy-3-phenylpropanoic acid (LHPPA). The weight average molar mass (Mw) of PLHPPA ranged from 3600 to 5300 and polydispersity index (Mw/Mn) from 1.0 to 1.4 when the reaction mixture was irradiated by microwave at 255, 340 and 510 w for 1 to 10 h, respectively.
Amorphous poly (L-2-hydroxy-3-phenylpropanoic acid) (PLHPPA) was synthesized by the microwave-assisted polycondensation of L-2-hydroxy-3-phenylpropanoic acid (LHPPA). The weight average molar mass (Mw) of PLHPPA ranged from 3600 to 5300 and polydispersity index (Mw/Mn) from 1.0 to 1.4 when the reaction mixture was irradiated by microwave at 255, 340 and 510 w for 1 to 10 h, respectively.
基金
The study is financially supported by the Research foundation of State Education Department of China and National 973 Project of China.