Cs Rb V series low temperature sulphuric acid catalyst was prepared for the first time by using carbonized mother liquor containing alkali metal salts. The results show that the conversion of SO 2 on catalyst prepared directly with carbonized mother liquor could reach to 24.8% at 410?℃. If n (Na)/ n (V) was adjusted properly, the conversion of SO 2 could be increased to 35.6% at 410?℃. Refined carbonized mother liquor could make the catalytic activity even higher at low temperature, the conversion of SO 2 could be increased to 36.65% at 410?℃. The catalyst was examined with differential thermal analysis. It was found that both endothermic peaks and exothermic peaks of catalyst shifted forward obviously and the catalyst possessed higher activity at low temperature.
Cs-Rb-V series low temperature sulphuric acid catalyst was prepared for the first time by using carbonized mother liquor containing alkali-metal salts. The results show that the conversion of SO(2) on catalyst prepared directly with carbonized mother liquor could reach to 24.8% at 410 degreesC. If n(Na)/n(V) was adjusted properly, the conversion of SO(2) could be increased to 35.6% at 410 degreesC. Refined carbonized mother liquor could make the catalytic activity even higher at low temperature, the conversion of SO(2) could be increased to 36.65% at 410 degreesC. The catalyst was examined with differential thermal analysis. It was found that both endothermic peaks and exothermic peaks of catalyst shifted forward obviously and the catalyst possessed higher activity at low temperature.
出处
《中国有色金属学会会刊:英文版》
CSCD
2001年第4期595-598,共4页
Transactions of Nonferrous Metals Society of China
基金
Project ( 5 95 0 40 0 5 )supportedbytheNationalNaturalScienceFoundationofChina