摘要
Al-7graphite composite was processed using Al-7graphite mushy prepared by electromagnetic-mechanical stirring method, and the influence of solid fraction on the distributing of graphite particles in ingot was studied. The results shows that the relationship between solid fraction and stirring temperature of mushy is: f(s) = 591.5-0.897 t (where f(s) is the solid fraction, t is the stirring temperature). For Al-7graphite composite, with the increasing of solid fraction, the aggregation extent of graphite particles reduced gradually, and when solid fraction was larger than 30%, graphite particles could distribute evenly in ingot.
Al-7graphite composite was processed using Al-7graphite mushy prepared by electromagnetic-mechanical stirring method, and the influence of solid fraction on the distributing of graphite particles in ingot was studied. The results shows that the relationship between solid fraction and stirring temperature of mushy is: f(s) = 591.5-0.897 t (where f(s) is the solid fraction, t is the stirring temperature). For Al-7graphite composite, with the increasing of solid fraction, the aggregation extent of graphite particles reduced gradually, and when solid fraction was larger than 30%, graphite particles could distribute evenly in ingot.
基金
China and Tsinghua-Zhongda Postdoctoral Science Foundation.]