The effect of hydrogen on the microstructures and superplasticity of a Ti3Al-Nb alloy was studied. The results showed that hydrogenation made the volume fraction of B2 phase increase and facilitated the dynamic recrystallization of the lath-like phase. The addition of hydrogen. reduced the flow stresses and made the maximum m value move to a lower temperature during the superplastic deformation. The superplastic deformation temperature of the alloy can be lowered by about 60 degreesC.
The effect of hydrogen on the microstructures and superplasticity of a Ti3Al-Nb alloy was studied. The results showed that hydrogenation made the volume fraction of B2 phase increase and facilitated the dynamic recrystallization of the lath-like phase. The addition of hydrogen. reduced the flow stresses and made the maximum m value move to a lower temperature during the superplastic deformation. The superplastic deformation temperature of the alloy can be lowered by about 60 degreesC.
作者
Hua Ding, Bingzhe Bai, Dingliang Wang, Dan Song, Caipei Zhang, Jianzhong Cui,Luyi Yang (Northeastern University, Shellyang 110006, China
Tsinghua University, Beijing 100084, China
Beijing Research Institute of Mechanical and Electrical Technology, Be
基金
The projeccgt is financially supported by the National Natural Science Foundation.Oundation.]