The embedded atom method (EAM) was used to study the order-disorder transformation in gamma -TiAl alloy with L1(0). structure at stoichiometrical composition, and the effect of lattice constants was also investigated. It was found that the gamma -TiAl alloy at stoichiometrical composition exhibits a second-order transition, and the relations between lattice constants a, c and the long-range order sigma are not linear. The lattice constant a decreases whereas c increases with the increase of the long-range order parameter. In this case the ordering induces the transformation from cubic to tetragonal. The change of the lattice constant during the ordering processes can be interpreted in terms of bond length.
The embedded atom method (EAM) was used to study the order-disorder transformation in gamma -TiAl alloy with L1(0). structure at stoichiometrical composition, and the effect of lattice constants was also investigated. It was found that the gamma -TiAl alloy at stoichiometrical composition exhibits a second-order transition, and the relations between lattice constants a, c and the long-range order sigma are not linear. The lattice constant a decreases whereas c increases with the increase of the long-range order parameter. In this case the ordering induces the transformation from cubic to tetragonal. The change of the lattice constant during the ordering processes can be interpreted in terms of bond length.
基金
This work was financially supported by the National Natural Science Foundation of China under Contract No.59895151-01