The submicron powder mixtures of TiC-TiN-WC-Mo-C-Ni sintered at 1400degreesC or below in vacuum were studied by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) analyses. The results showed that Mo2C formed at 800degreesC or below. Both WC and Mo2C disappeared at 1200degreesC, and TiN disappeared at 1250degreesC. In addition, the variations of lattice constants of the titanium carbonitride and nickel binder phase with sintering temperature were experimentally obtained, and the reason was analyzed.
The submicron powder mixtures of TiC-TiN-WC-Mo-C-Ni sintered at 1400degreesC or below in vacuum were studied by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) analyses. The results showed that Mo2C formed at 800degreesC or below. Both WC and Mo2C disappeared at 1200degreesC, and TiN disappeared at 1250degreesC. In addition, the variations of lattice constants of the titanium carbonitride and nickel binder phase with sintering temperature were experimentally obtained, and the reason was analyzed.
基金
This work wasfinancially supported by the National Natural Science Foundation Of China (50074017), the NationalDoctorate Progr