Microstructural evolution of TiAl base alloy during three-stepped thermo-mechanical treatment 被引量:1

Microstructural evolution of TiAl base alloy during three-stepped thermo-mechanical treatment
下载PDF
导出
摘要 A TiAl base alloy ingot with a height to diameter ratio of 2.2 was broken down by multiple step canned forging. The microstructures after every deformation and subsequent recrystallization were observed by optical microscopy. Results show that at the first step the reduction should be carefully controlled in case of double bulge and crack of the ingot. After the first annealing, recrystallization occurred at the deformed grain boundaries and inside the grain. The recrystallized microstructure is favorable for further deformation. After the second deformation and annealing, coarsening of the lamellae occurred and the microstructure became equiaxed. By the final deformation and subsequent recrystallization, the coarse lamellar colony can be refined to about 20 μm, and homogeneous microstructure was obtained from the ingot with a large initial height to diameter ratio. A TiAl base alloy ingot with a height to diameter ratio of 2.2 was broken down by multiple step canned forging. The microstructures after every deformation and subsequent recrystallization were observed by optical microscopy. Results show that at the first step the reduction should be carefully controlled in case of double bulge and crack of the ingot. After the first annealing, recrystallization occurred at the deformed grain boundaries and inside the grain. The recrystallized microstructure is favorable for further deformation. After the second deformation and annealing, coarsening of the lamellae occurred and the microstructure became equiaxed. By the final deformation and subsequent recrystallization, the coarse lamellar colony can be refined to about 20 μm, and homogeneous microstructure was obtained from the ingot with a large initial height to diameter ratio.
出处 《Journal of Central South University of Technology》 2001年第1期9-12,共4页 中南工业大学学报(英文版)
基金 TheNationalAdvancedMaterialsCommittee! (No .715 0 0 5 0 0 40 ) theNationalNaturalScienceFoundationofChina! (No.5 9895 15
关键词 TiAl base alloy hot forging MICROSTRUCTURE TiAl base alloy hot forging microstructure
  • 相关文献

参考文献12

  • 1J. A. Wert,M. F. Bartholomeusz.Effect of creep strain on microstructural stability and creep resistance of a TiAi/Ti3ai lamellar alloy[J].Metallurgical and Materials Transactions A.1996(1)
  • 2S. L. Semiatin,V. Seetharaman,V. K. Jain.Microstructure development during conventional and isothermal hot forging of a near-gamma titanium aluminide[J].Metallurgical and Materials Transactions A.1994(12)
  • 3KimYW.Orderedintermetallicalloys.PartⅢ :Gammati taniumaluminide[].Journal of Occupational Medicine.1995
  • 4LIUCT,MaziaszPJ.Roomandelevatedtemperatureme chanicalpropertiesofPMTiAlalloyTi 47Al 2Cr 2Nb[].GammaTitaniumAluminides.1995
  • 5Kim Y W.Gamma titanium aluminide[].Journal of Occupational Medicine.1994
  • 6Young Won Kim Materials and Manufacturing Directorate, Air Force Research Laboratory Wright Patterson AFB, OH 45433, U. S. A..WROUGHT TiAl ALLOY DESIGN[J].中国有色金属学会会刊:英文版,1999,9(S1):298-308. 被引量:3
  • 7Kim Y W.Microstructural evolution and mechanical properties of a forged gamma titanium aluminide alloy[].Acta Metallurgica et Materialia.1992
  • 8SEMIATIN S L,SEETHARAMAN V,JAIN V K.Microstructure development during conventional and isothermal hot forging of a near-gamma titanium aluminide[].Metallurgical and Materials Transactions.1994
  • 9Liu C T,Schneibel J H,Maziasz P J,et al.Tensile properties and fracture toughness of TiAl alloy with controlled microstructures[].Intermetallics.1996
  • 10Semiatin S L,Seetharaman V,Weiss I.Hot workability of titanium and titanium aluminide alloys—An overview[].Materials Science and Engineering.1998

共引文献2

同被引文献8

  • 1APPEL,WAGNER R.Microstructure and deformation of two-phase γ-titanium aluminide[J].Mater Sci Eng,1998,R22(5):187-262.
  • 2KIM Y W.Wrought Ti Al alloy design[J].Trans Nonferrous Met Soc China,1999,9(Supp 1):298-308.
  • 3CHEN G,ZHANG W,WANG Y,et al.Ti-Al-Nb intermetallic alloys based on the ternary intermetallic compound[A].Darolia R,Lewandowski J J,Liu CT,et al.Structural Intermetallics[M].Warrendale(PA):TMS,1993.319-324.
  • 4CHEN G,ZHANG W,LIU Z,et al.Microstructures and properties of high Nb containing TiAl alloys[A].Kim Y W,Dimiduk D M,Loretto M H.Gamma Titanium Aluminides[M].Warrendale(PA):TMS,1999.371-380.
  • 5SEMIATIN S L,SEETHARAMAN V,WEUSS I.Hot workability of titanium ahminide alloys-an overview[J]Mater Sci Eng,1998,A243:1-24.
  • 6MARTIN P L,RHODES C G.Thermomechanical processing effects on microstructure in alloy based on γ-TiAl[A].Darolia R,Lewandowski J J,Lju C T,et al.Structural Intermetallics[M].Warrendale(PA):TMS.1993.177-186.
  • 7闫蕴琪,王文生,张振祺,罗国轸,洪权,周廉.高Nb-TiAl基合金的开坯锻造[J].热加工工艺,2000,29(1):32-33. 被引量:3
  • 8王文生,阎蕴琪,王克光,周廉.高Nb-TiAl基合金锻压饼材的拉伸性能[J].理化检验(物理分册),2002,38(4):142-144. 被引量:1

引证文献1

二级引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部