Microstructure, tensile properties and compressive creep behaviors of Mg-(1.65–11.52) wt.% Sn-2 wt.% Nd alloys were studied in this paper. The microstructure of the as-cast Mg-Sn-Nd alloys consisted of dendritic α-Mg, Mg2Sn and Mg-Sn-Nd ternary phase containing rare earth element. The highest ultimate tensile strength of 140 MPa and percentage elongation after fracture of 9.7%, were achieved with a composition of Mg-8.23 wt.% Sn-2 wt.% Nd. The compressive creep resistance of Mg-8.23 wt.%Sn-2 wt.% Nd alloy w...
Microstructure, tensile properties and compressive creep behaviors of Mg-(1.65–11.52) wt.% Sn-2 wt.% Nd alloys were studied in this paper. The microstructure of the as-cast Mg-Sn-Nd alloys consisted of dendritic α-Mg, Mg2Sn and Mg-Sn-Nd ternary phase containing rare earth element. The highest ultimate tensile strength of 140 MPa and percentage elongation after fracture of 9.7%, were achieved with a composition of Mg-8.23 wt.% Sn-2 wt.% Nd. The compressive creep resistance of Mg-8.23 wt.%Sn-2 wt.% Nd alloy w...
基金
Project supported by the Science & Technology Bureau of Sichuan Province of China (03GG009-007-4)