The effect of Nd addition on the microstructure and mechanical properties of ZK20 magnesium alloy was investigated by room tensile test, optical microscopy, X-ray diffraction (XRD) and scanning electron microscopy (SEM) in order to develop a magnesium alloy with higher ductility. Results showed that the crystal grains of as-extruded ZK20+0.5%Nd magnesium alloy were effectively refined, and the alloy exhibited higher strength and ductility, with the UTS of 237 MPa and the elongation of 32.8%, increasing by 5...
The effect of Nd addition on the microstructure and mechanical properties of ZK20 magnesium alloy was investigated by room tensile test, optical microscopy, X-ray diffraction (XRD) and scanning electron microscopy (SEM) in order to develop a magnesium alloy with higher ductility. Results showed that the crystal grains of as-extruded ZK20+0.5%Nd magnesium alloy were effectively refined, and the alloy exhibited higher strength and ductility, with the UTS of 237 MPa and the elongation of 32.8%, increasing by 5...
基金
Project supported by the Major State Basic Reasearch and Development Program of China (973) (2007CB613700)
National Natural Science Foundation of China (50725413)
National Key Technologies R&D Program of China (2007BAQ00134-04)