The variation of microstucture and phase structure of metal Cr and Al powders prepared by high energy mechanical milling was analyzed and investigated.The results show that with the continuous balling the average grain sizes of the brittle Cr powders are gradually decreased,and the diffraction peaks are widened and the peak values lower owing to the interrelation caused by both cold welding and breaking;the tough Al powders exhibit intense cold welding,and most of powders lead to adhesion to ball surface and pot wall,meanwhile,the Al powders subjected to intense deformation have led to many dislocation rings with non dislocation wind up found in the microstructure.
The variation of microstucture and phase structure of metal Cr and Al powders prepared by high energy mechanical milling was analyzed and investigated.The results show that with the continuous balling the average grain sizes of the brittle Cr powders are gradually decreased,and the diffraction peaks are widened and the peak values lower owing to the interrelation caused by both cold welding and breaking;the tough Al powders exhibit intense cold welding,and most of powders lead to adhesion to ball surface and pot wall,meanwhile,the Al powders subjected to intense deformation have led to many dislocation rings with non dislocation wind up found in the microstructure.