This paper deals with gold extraction from a refractory concentrate by chlorine leaching.The process considers a pre-treatment of refractory materials by low temperature oxidation carried out with low oxygen concentration.The oxidized material is treated by leaching with brine.After gold adsorption/reduction onto activated carbon,iron and base metals can be precipitated by NaOH.Roasting tests show the necessity to carry out a thermal pre-treatment at least at 550°C to obtain a reduction of sulfur and mercury in the material(50%and 90%,respectively).Highest gold extraction yield(around 93%)is obtained in the leaching test performed with material sample treated at 650°C.This result confrms the necessity to optimize the thermal pre-treatment to improve Au recovery and to reduce chlorine consumption.A comparison with conventional cyanidation confrms that chlorination could be an useful alternative:in fact,gold extraction yield is quite low:57%in non-pre-treated material and 25%in pre-treatment material.
This paper deals with gold extraction from a refractory concentrate by chlorine leaching.The process considers a pre-treatment of refractory materials by low temperature oxidation carried out with low oxygen concentration.The oxidized material is treated by leaching with brine.After gold adsorption/reduction onto activated carbon,iron and base metals can be precipitated by NaOH.Roasting tests show the necessity to carry out a thermal pre-treatment at least at 550°C to obtain a reduction of sulfur and mercury in the material(50%and 90%,respectively).Highest gold extraction yield(around 93%)is obtained in the leaching test performed with material sample treated at 650°C.This result confrms the necessity to optimize the thermal pre-treatment to improve Au recovery and to reduce chlorine consumption.A comparison with conventional cyanidation confrms that chlorination could be an useful alternative:in fact,gold extraction yield is quite low:57%in non-pre-treated material and 25%in pre-treatment material.