Effect of Aging Temperature on Stress Corrosion Cracking of 17-4 PH Stainless Steel in Wet H_2S Environment

Effect of Aging Temperature on Stress Corrosion Cracking of 17-4 PH Stainless Steel in Wet H_2S Environment

导出

摘要 The effect of aging temperature on stress corrosion crocking of 17-4 precipitation-hardened(PH)stainless steel in simulated stimulant oil well environment was studied by the method B-NACE standard bent-beam test.It is found that when aging temperature ranges from 480 to 610℃,the sensitivity of hydrogen embrittlement decreases significantly. The effect of aging temperature on stress corrosion crocking of 17-4 precipitation-hardened(PH)stainless steel in simulated stimulant oil well environment was studied by the method B-NACE standard bent-beam test.It is found that when aging temperature ranges from 480 to 610℃,the sensitivity of hydrogen embrittlement decreases significantly.

作者 Zhou Chengshuang,Zheng Shuqi,Chen Changfeng,Lu Guiwu China University of Petroleum,Beijing 102249,China

出处《稀有金属材料与工程》 SCIE EI CAS CSCD 北大核心 2012年第S1期219-222,共4页 Rare Metal Materials and Engineering

基金 NSFC(50871122)

关键词 stress corrosion crocking(SSC) AGING temperature 17-4 precipitation-hardened STAINLESS steel hydrogen EMBRITTLEMENT stress corrosion crocking(SSC) aging temperature 17-4 precipitation-hardened stainless steel hydrogen embrittlement

分类号 TG171 [金属学及工艺—金属表面处理]

引文网络
相关文献

参考文献10

1F. Fantechi,,M. innocenti.Chloride stress corrosion cracking of precipitation hardening S.S. impellers in centrifugal compressor laboratory investigations and corrective actions[].Engineering Failure Analysis.2001
2C. N. Hsiao,C. S. Chiou,J. R. Yong.Aging reactions in a 17-4PH stainless steel[].Journal of Materials Chemistry.2002
3Salje,G.,Feller-Kniepmeier,M. Zeitschrift fur Metallkunde . 1978
4William F Smith."Structure and Properties of Engineering Alloys"[]..1993
5Chiang W C,Pu C C,Yu B L et al. Materials Letters . 2003
6Tsay L W,Yang T Y,Young M C. Materials Science and Engi- neering A . 2001
7Thompson R M,Kohut G B,Canfield D R et al. Corrosion . 1991
8NACE Standard TM0177-2005 . 2005
9Viswanathan U K,Banerjee S,Krishnan R. Journal of Materials Science . 1988
10Pound B G. Acta Metalurgica et Materialia . 1990

1LI Hongyu, SONG Xiping, WANG Yanli, and CHEN Guoliang State Key Lab for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing 100083, China.Characterization of γ′ precipitates in a nickel base superalloy quenching from aging temperature at different rates[J].Rare Metals,2010,29(2):204-208. 被引量：4
2GUO Shouren LU Dezhong GUO Jianting Institute of Metal Research,Academia,Shenyang,ChinaWU Xi Fushun Steel Works,Fushun,China Associate Professor,Institute of Metal Research,Academia Sinica,Shenyang 110015,China.EFFECTS OF AGING TEMPERATURE AND TIME ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF AN Fe-BASE SUPERALLOY[J].Acta Metallurgica Sinica(English Letters),1991,4(1):25-32. 被引量：1
3金亦富,SHENG Tianyuan,KONG Weicheng,ZHANG Ruihong,WANG Wenchang,孔德军.Effects of Strain Rate on Stress Corrosion of S355 Steel in 3.5% NaCl Solutions[J].Journal of Wuhan University of Technology(Materials Science),2016,31(6):1381-1386.
4Zitian FAN,Naiyu HUANG,Huafang WANG,Xuanpu DONG.Dry reusing and wet reclaiming of used sodium silicate sand[J].China Foundry,2005,2(1):38-43. 被引量：4
5Robert Fussik,Sebastian Weber.Local Microstructural Stability and Hydrogen Embrittlement of Iron-Base FCC Alloys[J].材料科学与工程（中英文A版）,2016,6(5):243-253.
6Zuo, Y,Latanision, RM.Effect of Strain Rate on Hydrogen Embrittlement Behaviour of Amorphous NiCrFeSiB Alloy[J].Journal of Materials Science & Technology,1996,12(2):105-108.
7Qing-He Zhao,Wei Liu,Yi-Chun Zhu,Bin-Li Zhang,Shuan-Zhu Li,Min-Xu Lu.Effect of Small Content of Chromium on Wet–Dry Acid Corrosion Behavior of Low Alloy Steel[J].Acta Metallurgica Sinica(English Letters),2017,30(2):164-175. 被引量：7
8刘多,张洪涛,杨轲,唐冬雁,冯吉才.Microstructure evolution of HAZ in the multi-pass underwater wet welded joints[J].China Welding,2013,22(1):30-34. 被引量：2
9Y Tan,D.H Zhouand J. Feng (Institute of Structural Mechanics, Chengdu 610003, China).INFLUENCE OF INTERNAL HYDROGEN ON THE HYDROGENEMBRITTLEMENT OF AUSTENITIC STAINLESS STEEL[J].Acta Metallurgica Sinica(English Letters),1997,10(3):228-232. 被引量：1
10Cui Lin,Xiaogang Li,Chaofang Dong.Pitting and galvanic corrosion behavior of stainless steel with weld in wet-dry environment containing Cl^-[J].Journal of University of Science and Technology Beijing,2007,14(6):517-522. 被引量：3

稀有金属材料与工程

2012年第S1期

浏览历史

内容加载中请稍等...

Effect of Aging Temperature on Stress Corrosion Cracking of 17-4 PH Stainless Steel in Wet H_2S Environment

参考文献10

相关作者

相关机构

相关主题

浏览历史