摘要
Thermal control coatings were fabricated by mixing of La1-xSrxMnO3(LSMO)powder and acrylic resin and brushed on Al alloy substrate.The powders of La0.7Sr0.3MnO3 and La0.8Sr0.2MnO3 were prepared using sol-gel method.XRD results reveal the phase structure of LSMO powders are perovskite.The transition temperature from metal to insulator of La0.7Sr0.3MnO3 and La0.8Sr0.2MnO3 are 300 and 275 K,respectively.The emissivity evolution with temperature of the coatings was measured.For La0.7Sr0.3MnO3/acrylic resin coating,the emissivity increases from 0.56 to 0.88,and for La0.7Sr0.3MnO3/acrylic resin coating from 0.50 to 0.90.
Thermal control coatings were fabricated by mixing of La1-xSrxMnO3(LSMO)powder and acrylic resin and brushed on Al alloy substrate.The powders of La0.7Sr0.3MnO3 and La0.8Sr0.2MnO3 were prepared using sol-gel method.XRD results reveal the phase structure of LSMO powders are perovskite.The transition temperature from metal to insulator of La0.7Sr0.3MnO3 and La0.8Sr0.2MnO3 are 300 and 275 K,respectively.The emissivity evolution with temperature of the coatings was measured.For La0.7Sr0.3MnO3/acrylic resin coating,the emissivity increases from 0.56 to 0.88,and for La0.7Sr0.3MnO3/acrylic resin coating from 0.50 to 0.90.
出处
《稀有金属材料与工程》
SCIE
EI
CAS
CSCD
北大核心
2012年第S1期253-255,共3页
Rare Metal Materials and Engineering
基金
NSFC(51001039)
National Basic Research Program of China(2007CB607602)
Fundamental Research Funds for the Central Universities(HIT.NSRIF.2009030)
Program of Excellent Teams of Harbin Institute of Technology