摘要
A series of tetracene-doped anthracene crystals with different doping concentrations(the highest mo-lar ratio 100:1) are grown from solution.Crystal structures and optical characteristics of the above mixed crystals are investigated at room temperature.By changing the doping concentrations,the fluorescence can be adjusted from blue-green to green and even to yellow-green.The emission spectra of anthracene/tetracene(An/Te) mixed crystals reveal the sensitized fluorescence of tetracene and the partial quenching of anthracene emission.The data of transient photoluminescence(PL) decays illus-trate that in An/Te mixed crystals,the decay of anthracene becomes faster,while the PL lifetime of tet-racene is longer than that of the tetracene single crystals.All above experimental results suggest that there is excitation energy transfer from anthracene to tetracene in the mixed crystals.
A series of tetracene-doped anthracene crystals with different doping concentrations (the highest molar ratio 100 1) are grown from solution. Crystal structures and optical characteristics of the above mixed crystals are investigated at room temperature. By changing the doping concentrations, the fluorescence can be adjusted from blue-green to green and even to yellow-green. The emission spectra of anthracene/tetracene (An/Te) mixed crystals reveal the sensitized fluorescence of tetracene and the partial quenching of anthracene emission. The data of transient photoluminescence (PL) decays illustrate that in An/Te mixed crystals, the decay of anthracene becomes faster, while the PL lifetime of tetracene is longer than that of the tetracene single crystals. All above experimental results suggest that there is excitation energy transfer from anthracene to tetracene in the mixed crystals.
基金
Supported by the National Natural Science Foundation of China (Grant No. 5057 3039)
the National Key Basic Research and Development Program of China (Grant No. 2006CB806200)