Nearly monodisperse,regular-shaped and well oil-dispersible tetragonal BaYF5:0.2Yb3+/0.02Er3+ nanocrystals(NCs) were synthesized in water-ethanol-oleic acid-sodium oleate system.The as-obtained NCs exhibited bright upconversion(UC) fluorescence under the 980 nm excitation.Blue(2H9/2-4I15/2),green((2H11/2,4S3/2)-4I15/2) and red(4F9/2-4I15/2) transitions were observed.The results indicated that the relative intensity of green to red increased gradually with increasing power density,which were seldom in the previous work.Therefore,the UC properties and mechanism were studied in detail.
Nearly monodisperse,regular-shaped and well oil-dispersible tetragonal BaYF5:0.2Yb3+/0.02Er3+ nanocrystals(NCs) were synthesized in water-ethanol-oleic acid-sodium oleate system.The as-obtained NCs exhibited bright upconversion(UC) fluorescence under the 980 nm excitation.Blue(2H9/2-4I15/2),green((2H11/2,4S3/2)-4I15/2) and red(4F9/2-4I15/2) transitions were observed.The results indicated that the relative intensity of green to red increased gradually with increasing power density,which were seldom in the previous work.Therefore,the UC properties and mechanism were studied in detail.
基金
Project supported by the National Natural Science Foundations of China (20876002,20976002)
Natural Science Foundation of Beijing (2082009,2091002)
Funding Project for Academic Human Resources Development in Institutions of Higher Learning under the Jurisdiction of Beijing Municipality