摘要
BaAl12O19:Tb,Ce phosphors were prepared by sol-gel technique,the crystalline structures of samples characterized by XRD,and the luminescence properties and energy transfer between Ce3+ and Tb3+ were investigated.The results indicated that the emission intensity and the excitation wavelength range of Tb3+ increased when Ce3+ was doped.It demonstrated that the Ce3+ added in the BaAl12O19:Tb could deliver energy to Tb3+,and Ce3+ was not luminous by itself.The relative emission intensity of Tb3+ at wavelength of 548 nm was the strongest by Tb3+/Ce3+ ratio of 2:1,when excited at 310 nm,which was the characteristic adsorption wavelength of Ce3+.
BaAl12O19:Tb,Ce phosphors were prepared by sol-gel technique,the crystalline structures of samples characterized by XRD,and the luminescence properties and energy transfer between Ce3+ and Tb3+ were investigated.The results indicated that the emission intensity and the excitation wavelength range of Tb3+ increased when Ce3+ was doped.It demonstrated that the Ce3+ added in the BaAl12O19:Tb could deliver energy to Tb3+,and Ce3+ was not luminous by itself.The relative emission intensity of Tb3+ at wavelength of 548 nm was the strongest by Tb3+/Ce3+ ratio of 2:1,when excited at 310 nm,which was the characteristic adsorption wavelength of Ce3+.
基金
Project supported by the Science and Technology Plan of Liaoning Province (2006223004)
the Doctor Foundation of Liaoning Province (20101083)
the Key Laboratory Project of the Education Department of Liaoning Province in China (2009S081)