摘要
In order to reduce the transverse corner cracks of high strength weathering steel Q450NQR1,the factors influencing transverse corner cracks on continuously cast slab,such as level fluctuation of molten steel in mold,mold taper,primary cooling,mold powder,secondary cooling,nitrogen content in steel,spray nozzle structure,processing parameters and equipment of CC,etc.,were analyzed.Based on this,a series of comprehensive countermeasures have been proposed.The operation shows by the use of key technologies,including stabilizing steel level,optimizing the mold taper,weakening the primary cooling and the secondary cooling,reforming the mold powder,and adjusting spray nozzle structure,the transverse corner cracks on continuously cast slab have been significantly reduced,and the edge cracks on hot rolled sheet have been eliminated due to the transverse corner cracks.The qualified slabs are delivered to produce weathering cold forming sectional steel,whose yield strength is greater than 450MPa.
In order to reduce the transverse corner cracks of high strength weathering steel Q450NQR1,the factors influencing transverse corner cracks on continuously cast slab,such as level fluctuation of molten steel in mold,mold taper,primary cooling,mold powder,secondary cooling,nitrogen content in steel,spray nozzle structure,processing parameters and equipment of CC,etc.,were analyzed.Based on this,a series of comprehensive countermeasures have been proposed.The operation shows by the use of key technologies,including stabilizing steel level,optimizing the mold taper,weakening the primary cooling and the secondary cooling,reforming the mold powder,and adjusting spray nozzle structure,the transverse corner cracks on continuously cast slab have been significantly reduced,and the edge cracks on hot rolled sheet have been eliminated due to the transverse corner cracks.The qualified slabs are delivered to produce weathering cold forming sectional steel,whose yield strength is greater than 450MPa.