A low carbon Nb-microalloyed high deformability pipeline steel with X100 grade has been processed by TMCP and followed two-stage cooling process.The microstructure is characterized by ferrite/bainite multiphase.The effective grain size is 1.85μm in average.The volume of ferrite is about 10-15% and the grains sizes are mostly less than 5μm.The bainite consists of granular-bainite and lath-bainite,with M/A islands finely dispersed.The longitudinal tensile yield strength,uniform elongation,yield ratio are 647MPa,7.6% and 0.78,respectively.Ferrite/bainite multiphase have large strain hardenability that resulting high strength and high deformability combination.Precipitation of Nb also improves the strength and uniform deformability by precipitation strengthening and grain refinement.
A low carbon Nb-microalloyed high deformability pipeline steel with X100 grade has been processed by TMCP and followed two-stage cooling process.The microstructure is characterized by ferrite/bainite multiphase.The effective grain size is 1.85μm in average.The volume of ferrite is about 10-15% and the grains sizes are mostly less than 5μm.The bainite consists of granular-bainite and lath-bainite,with M/A islands finely dispersed.The longitudinal tensile yield strength,uniform elongation,yield ratio are 647MPa,7.6% and 0.78,respectively.Ferrite/bainite multiphase have large strain hardenability that resulting high strength and high deformability combination.Precipitation of Nb also improves the strength and uniform deformability by precipitation strengthening and grain refinement.
作者
MENG De-liang 1,KANG Yong-lin 1,AN Shou-yong 2,XIA Dian-xiu 2,SUN Hao 2,ZHENG Xiao-fei 1 (1.School of Materials Science and Engineering,University of Science and Technology Beijing,Beijing 100083,China
2.Technology Center of Jinan Iron and Steel Co.,Ltd.,Jinan 250101,Shangdong,China)