摘要
The microstructural variations of hardened cement-fly ash pastes leached by soft water were investigated by MIP, XRD, TG and SEM. The results show that the mass of hardened cement-fly ash paste reduces and its microstructure deteriorates partly after leaching of soft water. At the leaching duration of 180 days, the hardened paste containing fly ash deteriorated a little more serious than the plain cement paste, but the incorporation of fly ash in a proper ratio was helpful to defer the trend of deterioration of the hardened paste microstructure. The microstructural stability of hardened cement-fly ash paste wasn’t damaged severely during the 180 days leaching duration.
The microstructural variations of hardened cement-fly ash pastes leached by soft water were investigated by MIP, XRD, TG and SEM. The results show that the mass of hardened cement-fly ash paste reduces and its microstructure deteriorates partly after leaching of soft water. At the leaching duration of 180 days, the hardened paste containing fly ash deteriorated a little more serious than the plain cement paste, but the incorporation of fly ash in a proper ratio was helpful to defer the trend of deterioration of the hardened paste microstructure. The microstructural stability of hardened cement-fly ash paste wasn’t damaged severely during the 180 days leaching duration.
基金
supported by the National Basic Research Program ("973" Project) (Grant No 2009CB623106)
the Key Project of Beijing Natu-ral Science Foundation (Grant No 8100001)