The hierarchical structure and mechanical property of shell nacre are experimentally investigated from the new aspects of chemical stability and chemistry-mechanics coupling. Through chemical deproteinization or demineralization methods together with characterization techniques at micro/nano scales,it is found that the nacre of abalone,haliotis discus hannai,contains a hierarchical structure stacked with irregular aragonite platelets and interplatelet organic matrix thin layers. Yet the aragonite platelet itself is a nanocomposite consisting of nanoparticles and intraplatelet organic matrix framework. The mean diameter of the nanoparticles and the distribution of framework are quite different for different platelets. Though the interplatelet and in-traplatelet organic matrix can be both decomposed by sodium hydroxide solution,the chemical stability of individual aragonite platelets is much higher than that of the microstructure stacked with them. Further,macroscopic bending test or nanoindentation experiment is performed on the micro/nanostructure of nacre after sodium hydroxide treatment. It is found that the Young's modulus of both the stacked microstructure and nanocomposite platelet reduced. The reduction of the microstructure is more remark than that of the platelet. Therefore the chemical-mechanical stability of the nanocomposite platelet itself is much higher than that of the stacked microstructure of nacre.
The hierarchical structure and mechanical property of shell nacre are experimentally investigated from the new aspects of chemical stability and chemistry-mechanics coupling. Through chemical deproteinization or demineralization methods together with characterization techniques at micro/nano scales,it is found that the nacre of abalone,haliotis discus hannai,contains a hierarchical structure stacked with irregular aragonite platelets and interplatelet organic matrix thin layers. Yet the aragonite platelet itself is a nanocomposite consisting of nanoparticles and intraplatelet organic matrix framework. The mean diameter of the nanoparticles and the distribution of framework are quite different for different platelets. Though the interplatelet and in-traplatelet organic matrix can be both decomposed by sodium hydroxide solution,the chemical stability of individual aragonite platelets is much higher than that of the microstructure stacked with them. Further,macroscopic bending test or nanoindentation experiment is performed on the micro/nanostructure of nacre after sodium hydroxide treatment. It is found that the Young’s modulus of both the stacked microstructure and nanocomposite platelet reduced. The reduction of the microstructure is more remark than that of the platelet. Therefore the chemical-mechanical stability of the nanocomposite platelet itself is much higher than that of the stacked microstructure of nacre.
基金
supported by the National Basic Research Program of China (Grant No. 2007CB936204)
the Program for Changjiang Scholars and Innovative Research Team in University of China (Grant Nos. 705021 and IRT0534)
the National Natural Science Foundation of China (Grant No. 10732040)
the Natural Science Foundation of Jiangsu Province (Grant No. BK2008042)