摘要
The compressive fracture characteristics of Zr-based bulk metallic glass under uniaxial compression tests are studied.The zigzag rheological behavior is observed in the compression stress-strain curves of amorphous alloys.At room temperature the uniaxial compression fracture takes place along the plane which is at a 45-degree angle to the direction of the compressive stress.The microstructure of a typical fracture pattern is the vein network.A unique,finger-like vein pattern is found to exist at the fracture surface of Zr-based bulk metallic glass.
The compressive fracture characteristics of Zr-based bulk metallic glass under uniaxial compression tests are studied.The zigzag rheological behavior is observed in the compression stress-strain curves of amorphous alloys.At room temperature the uniaxial compression fracture takes place along the plane which is at a 45-degree angle to the direction of the compressive stress.The microstructure of a typical fracture pattern is the vein network.A unique,finger-like vein pattern is found to exist at the fracture surface of Zr-based bulk metallic glass.
基金
supported by the National Natural Science Foundation of China (Grant No. 10905049)