摘要
High quality single crystal CrAs was grown by Sn flux method.The results of magnetic susceptibility and electrical resistivity are reported in a temperature range of 2 to 800 K.At low temperatures,a T2 dependence of resistivity is observed showing a Fermi-liquid behavior.The Kadowaki-Woods ratio is found to be 1×10-5 μΩ cm mol2 K2 mJ-2,which fits well to the universal value for many correlated electron systems.At about 270 K,a clear magnetic transition is observed with sharp changes of resistivity and susceptibility.Above 270 K,a linear-temperature dependence of the magnetic susceptibility is observed up to 700 K,which resembles the T-dependent magnetic susceptibility of parents of iron-pnictides superconductors.
High quality single crystal CrAs was grown by Sn flux method.The results of magnetic susceptibility and electrical resistivity are reported in a temperature range of 2 to 800 K.At low temperatures,a T2 dependence of resistivity is observed showing a Fermi-liquid behavior.The Kadowaki-Woods ratio is found to be 1×10-5 μΩ cm mol2 K2 mJ-2,which fits well to the universal value for many correlated electron systems.At about 270 K,a clear magnetic transition is observed with sharp changes of resistivity and susceptibility.Above 270 K,a linear-temperature dependence of the magnetic susceptibility is observed up to 700 K,which resembles the T-dependent magnetic susceptibility of parents of iron-pnictides superconductors.
基金
supported by the National Natural Science Foundation of China,the Knowledge Innovation Project of Chinese Academy of Sciences
the 973 Project of the MOST of China