摘要
Mortar prisms made with different cements or mineral admixtures plus 30% mass of limes tone filler were stored in 2% magnesium sulfate solution at 5±1 ℃ for 1 year and their visual appearance,strength development were measured at intervals.The formation of thaumasite was checked and confirmed by XRD and FTIR.The results show that the relative resistance to thaumasite form of sulfate attack of the cements is outlined below,from best to worst:sulphoaluminate cement,sulfate resisting Portland cement,OPC.The resistance to thaumasite form of sulfate attack of mortar is remarkably improved by the addition of silica fume or ground granulated blastfurnace slag (SL),and the better the resistance to thaumasite form of sulfate attack,the more the addition of SL is.The thaumasite form of sulfate attack is decreased to a certain degree by a lower replacement of cement with fly ash,but it is accelerated by the addition of a higher amount of fly ash due to its lower reactivity.
Mortar prisms made with different cements or mineral admixtures plus 30% mass of limes tone filler were stored in 2% magnesium sulfate solution at 5±1 ℃ for 1 year and their visual appearance,strength development were measured at intervals.The formation of thaumasite was checked and confirmed by XRD and FTIR.The results show that the relative resistance to thaumasite form of sulfate attack of the cements is outlined below,from best to worst:sulphoaluminate cement,sulfate resisting Portland cement,OPC.The resistance to thaumasite form of sulfate attack of mortar is remarkably improved by the addition of silica fume or ground granulated blastfurnace slag (SL),and the better the resistance to thaumasite form of sulfate attack,the more the addition of SL is.The thaumasite form of sulfate attack is decreased to a certain degree by a lower replacement of cement with fly ash,but it is accelerated by the addition of a higher amount of fly ash due to its lower reactivity.