A novel Er (3+)-doped (ZnO)(P_2O_5)(B_2O_3) glass with excellent optical properties was prepared. The glasses were proved to have high stability by the investigation of the durability in boiling water. The properties of their spectra at about 1.5 μm change a lot with the concentrations of both Er (3+) and B_2O_3. Compared with Er (3+)-doped into the borate glass and the zinc phosphate glass,the glass prepared in our laboratory shows a larger quenching concentration and a much broader emission band at 1.54 μm.
A novel Er (3+)-doped (ZnO)(P_2O_5)(B_2O_3) glass with excellent optical properties was prepared. The glasses were proved to have high stability by the investigation of the durability in boiling water. The properties of their spectra at about 1.5 μm change a lot with the concentrations of both Er (3+) and B_2O_3. Compared with Er (3+)-doped into the borate glass and the zinc phosphate glass,the glass prepared in our laboratory shows a larger quenching concentration and a much broader emission band at 1.54 μm.
基金
SupportedbyNaturalScienceFoundationofChina (10 2 740 82 )andYouthScienceResearchFoundationofChangchunInstituteofOptics ,FineMechanicsandPhysics ,ChineseAcademyofSciences