Nd:NaBi(WO_4)_2 crystals (Nd:NBW) were grown by Czochralski method. The pulling rate is 0.3 mm·h (-1),and the rotational speed of Nd:NBW crystal is 2 r·min (-1). The components of this single crystal were determined by X-ray diffractions,and its corresponding properties were described from thermal gravity and differential thermal analysis experiments. The absorption cross-sections were calculated. The emission band of Nd:NBW crystal was obtained from its luminous spectrum.
Nd:NaBi(WO_4)_2 crystals (Nd:NBW) were grown by Czochralski method. The pulling rate is 0.3 mm·h (-1),and the rotational speed of Nd:NBW crystal is 2 r·min (-1). The components of this single crystal were determined by X-ray diffractions,and its corresponding properties were described from thermal gravity and differential thermal analysis experiments. The absorption cross-sections were calculated. The emission band of Nd:NBW crystal was obtained from its luminous spectrum.