摘要
TiO_2-CeO_2 nanocomposite particles were prepared with Ce(NO_3)_3·6H_2O and TiCl_4 as precursors by the codeposition method and supercritical fluid drying (SCFD) technology. The particles prepared were characterized by means of XRD, TEM and FTIR. The results show that SCFD can give rise to the direct synthesis of the anatase TiO_2-CeO_2,and the particle size is 6~11 nm under 500 ℃ thermal-treated,smaller than that by common drying (CD). The phase transformation from anatase to rutile is inhibited by supercritical fluid drying technology. The peak of CeO_2 is not observed in XRD patterns,Ce-O band vibration was present in FTIR spectrum,which indicates that CeO_2 is well dispersed on the surface of TiO_2.
TiO_2-CeO_2 nanocomposite particles were prepared with Ce(NO_3)_3·6H_2O and TiCl_4 as precursors by the codeposition method and supercritical fluid drying (SCFD) technology. The particles prepared were characterized by means of XRD, TEM and FTIR. The results show that SCFD can give rise to the direct synthesis of the anatase TiO_2-CeO_2,and the particle size is 6~11 nm under 500 ℃ thermal-treated,smaller than that by common drying (CD). The phase transformation from anatase to rutile is inhibited by supercritical fluid drying technology. The peak of CeO_2 is not observed in XRD patterns,Ce-O band vibration was present in FTIR spectrum,which indicates that CeO_2 is well dispersed on the surface of TiO_2.
基金
ProjectsupportedbytheNationalDevelopmentProjectofHighTechnology (863 ,2 0 0 1AA3 2 2 0 3 0 )andtheNationalNaturalScienceFoundationofChina (2 0 0 760 0 4)